CFRT Laminates

CFRT Laminates
CFRT Laminates CFRT Laminates CFRT Laminates

CFRT Laminates

Item No.: LM-002
CFRT Laminates in black color.
INQUIRY
Description Application
Introduction
CFRT Laminates is a new type of pp composite which is reinforced by continuous fiber-glass unidirectional tape. By a special processing technique, the pp and fiber-glass tape are fused excellently, which makes it able to realize the second time of thermoforming.
It has many features, including light weight, high compressive strength, and environmentally friendly, etc. It can replace FRP panels and metal sheets. It is able to be produced continuously and supplied in rolls and it finds great applications in containers, trucks, labor protection, building, etc.

Parameters
The mechanical properties
Thickness (MM)Test Standard Density Test Standard Test Item Performance Index Value
2.00 1.5 GB/T1447-2005 Tensile Modulus of Elasticity (GPa) 11.74
Tensile Strength (MPa) 291.5
GB/T1449-2005 Bending Modulus of Elasticity  (GPa) 13.43
Flexural Strength (MPa) 274.85
GB/T1843-2008 Impact Strength Impact-Resistance Strength（KJ/㎡） ≥150

Ageing-resistant Performance
Test Method: Place certain samples in an oven with forced air circulation, which is maintained at 110℃ for 500 h, which amounts to putting the same samples in natural environment for 5 years. 
Thickness(MM) Reference Standard Test Item Performance Index Before Test After Test
2.00 GB/T1447-2005 tensile Modulus of Elasticity (GPa) 11.74 12.10
Tensile Strength (MPa) 291.5 288
GB/T1449-2005 bending Modulus of Elasticity (GPa) 13.43 11.00
Flexural Strength (MPa) 274.85 254.47

The tensile strength test after 100 h of UV exposure
Test Condition
Test Parameter Reference Standard
Power Radiancy Loop Parameter Temperature Test Period GB/T 16422.3-1997
UV340 0.76W/m³
@340nm		 Illumination time：8h
Condensation time：4h		 Illumination 60 ±3℃
Condensation 50 ± 3℃		 100h
 

Test Result
Standard Index Before After
GB/T1447-2005 Tensile Strength (MPa) 291.5 257
Tensile Modulus (GPa) 11.74 11.44

Specifications
Standard Thickness（MM） Width（MM） Length（M）
Supplied in rolls 0.5-3 1100-2800 ≤1000
Refrigerated Container
Field of Application: Two sides and Top of the Container, 
Advantage: Heat Insulation, Light weight, Corrosion resistance

Refrigerated Truck
Field of Application: Two sides and Top of the Container, 
Advantage: Easy to assemble, Heat Insulation, Light weight, Corrosion resistance

Sneakers
Field of Application: Sole Cushion
Advantage: light weight, good elasticity, energy absorbing, abrasion resistance, corrosion resistance, suitable for hot melting welding

Seats
Field of Application: backrest
Advantage: light weight, high compressive strength

Luggage
Field of Application: Case of luggage
Advantage: light weight, high compressive strength
Dean Ava
Dean Ava
Dean Ava